China Factory for Transformer Cut Core - Fe-Based 1K107 Nanocrystalline Ribbon – Malio
China Factory for Transformer Cut Core - Fe-Based 1K107 Nanocrystalline Ribbon – Malio Detail:
Description
| Product Name | Fe-Based 1K107 Nanocrystalline Ribbon |
| P/N | MLNR-2132 |
| Width | 5-65mm |
| Thickness | 26-34μm |
| Saturation magnetic induction | 1.25 Bs (T) |
| Coercivity | 1.5 Hc (A/m) |
| Resistivity | 1.20 （μΩ·m ） |
| Magnetostriction coefficient | 1 λs (ppm) |
| Curie temperature | 570 Tc (℃) |
| Crystallization temperature | 500 Tx (℃) |
| Density | 7.2 ρ (g/cm3) |
| Hardness | 880 |
| Thermal expansion coefficient | 7.6 |
Application
● Switching power supply transformers and pulse transformer cores
● Power transformers, precision current transformer cores
● Leakage protection switch transformer iron core
● Filter inductors, energy storage inductors, reactor cores
● EMC common mode and differential mode inductor core
● Saturation reactors, magnetic amplifiers, spike suppressor cores and magnetic beads
Features
Fe-based Nanocrystalline materials are superior to conventional materials and will be the best solution for your application (Figure 1.1).
Figure 1.1 μr versus Bs of different soft magnetic materials
● High saturation magnetic induction (1.25 T) and high magnetic permeability (>80,000) for small volumes and high precision
● Core loss equivalent to 1/5 of iron-based amorphous, with losses as low as 70 W/kg at 100 kHZ, 300 mT
● Saturation magnetostriction coefficient close to 0, with very low operating noise
● Excellent temperature stability, <10% change in material properties over the temperature range -50 to 120 °C
● Excellent frequency characteristics with excellent permeability and low losses over a wide frequency range
● With adjustable magnetic properties, different types of magnetic properties can be obtained by applying different transverse and vertical magnetic fields, or without magnetic field heat treatment, such as low remanence, high rectangular ratio, and high magnetic permeability
Material comparison
| Performance Comparison of Fe-based Nanocrystalline Ribbon with Ferrite Core | ||
|
Basic parameters |
Nanocrystalline Ribbon |
Ferrite Core |
| Saturation magnetic induction Bs (T) |
1.25 |
0.5 |
| Residual magnetic induction Br (T)(20KHz) | ＜0.2 | 0.2 |
| Core losses (20KHz/0.2T)(W/kg) | ＜3.4 | 7.5 |
| Core losses (20KHz/0.5T)(W/kg) | ＜35 | Cannot be used |
| Core losses (50KHz/0.3T)(W/kg) | ＜40 | Cannot be used |
| Magnetic Conductivity (20KHz) (Gs/Oe) | ＞20000 | 2000 |
| Coercive force Hc (A/m) | ＜2.0 | 6 |
| Resistivity (mW-cm) | ＜2 | 4 |
| Saturated magnetostriction coefficient（X10-6） | 400 | 740 |
| Resistivity(mW-cm) | 80 | 106 |
| Curie Temperature | ＞0.7 | - |
Product detail pictures:
Related Product Guide:
Our rewards are lower costs,dynamic profits team,specialised QC,potent factories,high-quality services for China Factory for Transformer Cut Core - Fe-Based 1K107 Nanocrystalline Ribbon – Malio , The product will supply to all over the world, such as: Gambia, Anguilla, Toronto, Our company has already have pass the ISO standard and we're fully respect our customer 's patents and copyrights. If the customer provides their own designs, We will guarantee that they will likely be the only one can have that merchandise. We hoping that with our good products can bring our customers a great fortune.
By Athena from Kazakhstan - 2018.11.28 16:25
The customer service staff is very patient and has a positive and progressive attitude to our interest, so that we can have a comprehensive understanding of the product and finally we reached an agreement, thanks!
By Cheryl from Norway - 2017.05.31 13:26