We will make just about every exertion for being excellent and perfect, and speed up our actions for standing during the rank of worldwide top-grade and high-tech enterprises for Choke Coil Filter Inductor, Current Transducer, Current Transformer For Energy Meter, Our intention should be to assist customers comprehend their goals. We have been creating terrific endeavours to obtain this win-win circumstance and sincerely welcome you to definitely join us!

Good User Reputation for Amorphous Bars - Fe-Based 1K107 Nanocrystalline Ribbon – Malio Detail:

Description

Product Name	Fe-Based 1K107 Nanocrystalline Ribbon
P/N	MLNR-2132
Width	5-65mm
Thickness	26-34μm
Saturation magnetic induction	1.25 Bs (T)
Coercivity	1.5 Hc (A/m)
Resistivity	1.20 （μΩ·m ）
Magnetostriction coefficient	1 λs (ppm)
Curie temperature	570 Tc (℃)
Crystallization temperature	500 Tx (℃)
Density	7.2 ρ (g/cm3)
Hardness	880
Thermal expansion coefficient	7.6

Application

● Switching power supply transformers and pulse transformer cores

● Power transformers, precision current transformer cores

● Leakage protection switch transformer iron core

● Filter inductors, energy storage inductors, reactor cores

● EMC common mode and differential mode inductor core

● Saturation reactors, magnetic amplifiers, spike suppressor cores and magnetic beads

Features

Fe-based Nanocrystalline materials are superior to conventional materials and will be the best solution for your application (Figure 1.1).

Figure 1.1 μr versus Bs of different soft magnetic materials

● High saturation magnetic induction (1.25 T) and high magnetic permeability (>80,000) for small volumes and high precision

● Core loss equivalent to 1/5 of iron-based amorphous, with losses as low as 70 W/kg at 100 kHZ, 300 mT

● Saturation magnetostriction coefficient close to 0, with very low operating noise

● Excellent temperature stability, <10% change in material properties over the temperature range -50 to 120 °C

● Excellent frequency characteristics with excellent permeability and low losses over a wide frequency range

● With adjustable magnetic properties, different types of magnetic properties can be obtained by applying different transverse and vertical magnetic fields, or without magnetic field heat treatment, such as low remanence, high rectangular ratio, and high magnetic permeability

Material comparison

Performance Comparison of Fe-based Nanocrystalline Ribbon with Ferrite Core
Basic parameters	Nanocrystalline Ribbon	Ferrite Core
Saturation magnetic induction Bs (T)	1.25	0.5
Residual magnetic induction Br (T)(20KHz)	＜0.2	0.2
Core losses (20KHz/0.2T)(W/kg)	＜3.4	7.5
Core losses (20KHz/0.5T)(W/kg)	＜35	Cannot be used
Core losses (50KHz/0.3T)(W/kg)	＜40	Cannot be used
Magnetic Conductivity (20KHz) (Gs/Oe)	＞20000	2000
Coercive force Hc (A/m)	＜2.0	6
Resistivity (mW-cm)	＜2	4
Saturated magnetostriction coefficient（X10^-⁶）	400	740
Resistivity(mW-cm)	80	10⁶
Curie Temperature	＞0.7	-

Product detail pictures:

Related Product Guide:

We offer fantastic energy in high quality and enhancement,merchandising,profits and promoting and procedure for Good User Reputation for Amorphous Bars - Fe-Based 1K107 Nanocrystalline Ribbon – Malio , The product will supply to all over the world, such as: Montpellier, Italy, Bogota, Our staffs are adhering to the "Integrity-based and Interactive Development" spirit, and the tenet of "First-class Quality with Excellent Service". According to the needs of every customer, we give customized & personalised services to help customers achieve their goals successfully. Welcome clients from home and abroad to call and inquire!